| Type |
Two-component polyester saturated aliphatic urethane finish. |
| Color |
19 Colors (see colorchart). Custom colors on request. |
| Gloss |
Ultra high gloss |
| Recommended use |
Exterior topsides and interior use. Finishing coat for fiberglass, steel, aluminum and wood. For use on all epoxy primed substrates or direct application on unpainted wood or thoroughly cleaned and degreased fiberglass surfaces above the waterline. |
| Properties |
Excellent resistance to abrasion, weathering, chemicals and loss of gloss. The outstanding flow characteristics make this two-component topcoat highly suitable for both brush, roller and spray application. |
| Container Size |
750 ml. (500 gr. base + 250 gr. reactor = 750 gr. mixed) 2:1 mix by weight. |
| Density |
1.00 - 1.40 kg./liter (mixed product) (depending on color) |
| Solids Content |
50 - 55 +/- 2 vol. % (mixed product) (depending on color) |
| Recommended film
thickness |
Per coat wet 80 micron
Per coat dry 40-45 micron |
| Application |
Brush, roller, conventional air spray, H.V.L.P. |
Application
-brush or roller
-air spray
|
Thin 0 - 10 % with Epifanes P.U. Brushthinner
Thin up to 10 % with Epifanes P.U. Spraythinner. Spray viscosity 20-22 sec.
DIN cup 4 - Nozzle 1.8 mm., pressure 2 - 3 Bar. Apply light tack coat to fully
wet the surface. Allow 15 - 20 min. to dry, then fully spray the entire surface.
Airless spray not advised. |
| Drying times at 65F / 65% RH |
Tack free - 3 hours Tape free - 7 hours
Dry - 8 hours Recoatable - 24 hours
|
| Application conditions |
Temperature should be between 50F. and 85F. during application. Air humidity below 85%. Avoid painting in too much wind or sun. A rapid loss of solvents will occur under these conditions and will decrease the flowing ability. Add thinner up to the specified percentage to compensate for the faster release of solvents. |