Golspar Satin is a dull gloss varnish ideal for anywhere a low-lustre, dull gloss effect is desired, such as cabinets tables counters etc. Resists scratches and alcohol stains. Creates a warm look. Goldspar Satin is a low luster modified urethane varnish, designed for application to interior wood surfaces.
Available in Pint and Quart sizes.
|Drying Information||50 Degrees F||73 Degrees F||95 Degrees F|
|Touch Dry (ISO)||3 hours||2 hours||1 hour|
|Goldspar Satin||16 hours-||12 hours-||8 hours-|
BARE WOOD: Sand with 80 grade (grit) paper. Wipe with Brushing Liquid 333. Apply sealer coat of varnish reduced 10% with Brushing Liquid 333.
PREVIOUSLY VARNISHED WOOD: In Good Condition Sand surface with 120-150 grade (grit) paper and remove all dust. In Poor Condition If varnish is badly checked or peeling, remove finish to bare wood with Interstrip Semi-Paste 299E. Follow directions for varnishing bare wood.
Method Apply at least 5-6 coats on bare wood and a minimum of 3 coats on previously varnished surfaces until a satisfactory finish is obtained. Sand between each coat with 220 grade (grit) paper. Remove sanding residue with a rag dampened with Brushing Liquid 333.
Thinner Brush - Brushing Liquid 333. Spray - Special Thinner 216.
Cleaner Bare Wood - Brushing Liquid 333.
Ventilation and Humidity Control It is best to paint on warm, dry mornings. Cold weather retards the drying and humidity can spoil the gloss. Be sure to have good ventilation when applying Rubbed Effect and through its drying time.
Airless Spray Pressure: 170 bar/2500 psi. Tip Size: 0.33-0.41 mm/13-16 thou.
Conventional Spray Pressure Pot: Pressure: 3.44-4.47 bar/50-65 psi (gun pressure); 8-10 psi (pot pressure). Tip Size: 1.0-1.4 mm/40-50 thou. Siphon Cup: Pressure: 3.44-4.47 bar/50-65 psi - gun pressure. Tip Size: 1.5-1.8 mm/60-70 thou.
Brush Always use a clean brush that is kept specifically for varnishing. Clean brushes before use.
Roller If rolling, use a thin nap roller and "tip-off" with a clean natural bristle brush.
Other Spray pressures listed are recommendations only. The applicator may use any settings which yield the best results for the individual spraying technique and current weather conditions. To enhance appearance of the bare wood and fill porous open grain, apply Interstain according to label directions and allow to dry overnight.
Some Important Points Excessive wet film thickness (more than 5 mils WFT) may result in poor and uneven gloss. Never leave bare wood exposed for long periods of time as it will absorb moisture. Avoid using Goldspar Satin straight from the can as this will cause it to age prematurely and may introduce contamination to the can. Failure to follow proper dry times carefully will cause improper drying, wrinkling and loss of adhesion. Avoid painting in direct sunlight. Product temperature should be minimum 10 deg C/50 deg F and maximum 29 deg C/85 deg F. Ambient temperature should be minimum 10 deg C/50 deg F and maximum 35 deg C/95 deg F. Substrate temperature should be minimum 10 deg C/50 deg F and maximum 29 deg C/85 deg F.
Compatibility/Substrates Apply to clean, dry, properly prepared surfaces only. Goldspar Satin can be applied over any varnish as long as it is adhered well and has been cleaned and sanded. Do not apply two part varnishes over Goldspar Satin.
Number of Coats At least 5-6 coats Bare Wood: Thin first coat 10%
Coverage (Theoretical) - 525 (sq ft/Gal) by brush, 420 (sq ft/Gal) by spray
Application Methods Brush, Roller, Airless Spray, Conventional Spray - Pressure Pot or Siphon Cup
Phasellus suscipit tincidunt tristique. Quisque mattis euismod ipsum, ac accumsan ante fermentum non. Vestibulum eget auctor lorem. Integer euismod justo nulla, nec ultricies ipsum pulvinar in. Duis sed fringilla turpis, at ultricies orci. Nam est turpis, consequat nec feugiat a.
Praesent sodales et ipsum
Mauris congue justo sit amet lacus sagittis, a tempor lectus tempus. Suspendisse quis nulla ac nibh accumsan tincidunt ac quis tortor. Proin dignissim aliquam odio, sed bibendum urna sagittis dapibus. Aenean ut tristique ante, sit amet ultrices nisi. Praesent eu dapibus augue. Mauris tempus suscipit ipsum, et malesuada tellus euismod eu. Quisque consequat turpis id feugiat lacinia. Vestibulum sit amet elementum augue. Quisque tempus ligula vitae placerat pulvinar. In egestas sodales lorem, id egestas lacus pharetra eget. Sed ac mi placerat, placerat nulla ut, imperdiet nunc. Mauris at felis vehicula, commodo est eu, ullamcorper purus.